BRASS STRIP TO SPECIFICATION BS EN 1652-1998 DESIGN CUZN37MATERIAL CONDITION R550 WITH UTS 55-65 KGF/MM2,ELONGATION 4%MIN. TO SIZE 0.6 - 0.06MM THICK X 12 MM WIDE IN COIL FORM (REF.DRG.NO.BW8.388.004)
Specification
BRASS STRIP TO SPECIFICATION BS EN 1652-1998 DESIGN CUZN37MATERIAL CONDITION R550 WITH UTS 55-65 KGF/MM2,ELONGATION 4%MIN. TO SIZE 0.6 - 0.06MM THICK X 12 MM WIDE IN COIL FORM(REF.DRG.NO.BW8.388.004)
ALUMINIUM ALLOY ROUNDS TO SPECN. IS:733-1983 REAFFIRMED 2006 GRADE 24345 IN WP CONDITION HAVING STRAIGHT LENGTH OF 2 TO 3 METERS , SIZE : 10+/-0.1 MM DIA WITHOUT PGG.
Specification
ALUMINIUM ALLOY ROUNDS TO SPECN. IS:733-1983 REAFFIRMED 2006 GRADE 24345 IN WP CONDITION HAVING STRAIGHT LENGTH OF 2 TO 3 METERS , SIZE : 10+/-0.1 MM DIA WITHOUT PGG.
ALUMINIUM ALLOY ROD TO SPECN. IS:733 REAFFERMED 2006 GR. 24345 IN WP CONDITION. SIZE: 14 +/-0.1 MM DIA HAVING STRAIGHT LENGTH OF MINIMUM 1.5 METERS AND 1 MM MAXIMUM PGG ON RADIUS.
Specification
ALUMINIUM ALLOY ROD TO SPECN. IS:733 REAFFERMED 2006 GR. 24345 IN WP CONDITION. SIZE: 14 +/-0.1 MM DIA HAVING STRAIGHT LENGTH OF MINIMUM 1.5 METERS AND 1 MM MAXIMUM PGG ON RADIUS.
CONTAINER CARTRIDGE SEMI FINISHED TO OFAJ DRAWING NO FS2956C(ONLY ONE RAW MATERIAL TO BE USED FOR ENTIRE CONSIGNMENT OF A SINGLE S.O. FIRMS TO INDICATE THE SAME IN THE QUOTATION).
Specification
CONTAINER CARTRIDGE SEMI FINISHED TO OFAJ DRAWING NOFS2956C(ONLY ONE RAW MATERIAL TO BE USED FOR ENTIRE CONSIGNMENT OF A SINGLE S.O. FIRMS TO INDICATE THE SAME IN THE QUOTATION).
EXTRUDED ALUMINIUM ALLOY TUBE TO SPECN.DTD-5124 (LATEST ISSUE) IN "T6" CONDITION HAVING STRAIGHTNESS OF 0.4 MM, CONCENTRICITY BETWEEN INNER AND OUTER DIAMETER 0.5 MM SIZE: 70+1.5/-0.5 MM O/D X 58+1.5-0.5 MM I/D X 465 + 5 MM LONG
Specification
EXTRUDED ALUMINIUM ALLOY TUBE TO SPECN.DTD-5124 (LATEST ISSUE) IN "T6" CONDITION HAVING STRAIGHTNESS OF 0.4 MM, CONCENTRICITY BETWEEN INNER AND OUTER DIAMETER 0.5 MM SIZE: 70+1.5/-0.5 MM O/D X 58+1.5-0.5 MM I/D X 465 + 5 MM LONG
COLD ROLLED ALUMINIUM ALLOY SHEET TO SPECN. IS:736(LATEST ISSUE) GRADE 65032 IN "M" CONDITION (TEST PIECE TO BE TESTED IN "WP" CONDITION) MATERIAL SHOULD BE CAPABLE FOR FLOW TURNING.SIZE:-9.5 +/- 0.2MM THICK X 914MM WIDE X 2438MM LONG.
Specification
COLD ROLLED ALUMINIUM ALLOY SHEET TO SPECN. IS:736(LATEST ISSUE) GRADE 65032 IN "M" CONDITION (TEST PIECE TO BE TESTED IN "WP" CONDITION) MATERIAL SHOULD BE CAPABLE FOR FLOW TURNING.SIZE:-9.5 +/- 0.2MM THICK X 914MM WIDE X 2438MM LONG.
CARBON STEEL BRIGHT ROUNDS TO SPECN. BS:970 PT.I-1983 GRADE O80M40 CONDITION NORMALISED IN STRAIGHT LENGTH OF 3 METERS WITH 10% SHORTS DOWN TO 2-3 METRES SIZE: 35.00 - 0.1 MM DIA.
Specification
CARBON STEEL BRIGHT ROUNDS TO SPECN. BS:970 PT.I-1983 GRADE O80M40 CONDITION NORMALISED IN STRAIGHT LENGTH OF 3 METERS WITH 10% SHORTS DOWN TO 2-3 METRES SIZE: 35.00 - 0.1 MM DIA.
ELECTROLYTIC TOUGH PITCH HIGH CONDUCTIVITY COPPER (ETP) INGOT WITH MINIUM COPPER CONTENT OF 99.9% AS PER SPECN. IS:191 PT V - 1980, CAST AS NOTCHED BAR/SLAB EACH WEIGHING 25 KG.APPROX
Specification
ELECTROLYTIC TOUGH PITCH HIGH CONDUCTIVITY COPPER (ETP) INGOT WITH MINIUM COPPER CONTENT OF 99.9% AS PER SPECN. IS:191 PT V - 1980, CAST AS NOTCHED BAR/SLAB EACH WEIGHING 25 KG.APPROX